LATIGEA B20 AM UVH

$1.00

LATIGEA B20 AM UVH is a 100% biobased PLA (polylactic acid) technical compound. Easily processable and colourable, UV- and hydrolysis-stabilised, it has a heat resistance above 100°C after annealing. Optimised for both 3D printing from filament (FFF) and direct 3D printing from granule (FGF).

Base polymer PLA HT

Fillers/Reinforcements Unfilled

Chemical-physical properties UV- and hydrolysis-stabilised
Thermal properties Improved thermal resistance
“Green” version Biobased
3D Printing Suitable also for printing from granule
Granule drying conditions 60°C
Filament extrusion conditionsExtrusion temperature: 200°C – 210°C
Filament drying temperature: 60°C
3D printing conditionsExtruder temperature: 195°C – 210°C
Bed temperature: 0°C – 50°C
Cooling: ON
Post-annealing conditions: 100°C 1h
Richiedi info
SKU: 37110BA Categories: , Product ID: 25910

Description

LATIGEA B20 AM UVH is a 100% biobased PLA (polylactic acid) technical compound. Easily processable and colourable, UV- and hydrolysis-stabilised, it has a heat resistance above 100°C after annealing. Optimised for both 3D printing from filament (FFF) and direct 3D printing from granule (FGF).

Base polymer PLA HT

Fillers/Reinforcements Unfilled

Chemical-physical properties UV- and hydrolysis-stabilised
Thermal properties Improved thermal resistance
“Green” version Biobased
3D Printing Suitable also for printing from granule
Granule drying conditions 60°C
Filament extrusion conditionsExtrusion temperature: 200°C – 210°C
Filament drying temperature: 60°C
3D printing conditionsExtruder temperature: 195°C – 210°C
Bed temperature: 0°C – 50°C
Cooling: ON
Post-annealing conditions: 100°C 1h
Richiedi info

Additional information

Disponibile in

,

Polimero base

Filler/rinforzi
Versione “green”

Proprietà termiche

Proprietà fisiche

Stampa 3D

Categoria

RequestDataSheet

Download

Info


This will close in 0 seconds

Datasheet


This will close in 0 seconds

Iscrizione alla newsletter


This will close in 0 seconds

Subscribe our newsletter


This will close in 0 seconds